Precision wood particle feedstocks

ABSTRACT

Wood particles having fibers aligned in a grain, wherein: the wood particles are characterized by a length dimension (L) aligned substantially parallel to the grain, a width dimension (W) normal to L and aligned cross grain, and a height dimension (H) normal to W and L; the L×H dimensions define two side surfaces characterized by substantially intact longitudinally arrayed fibers; the W×H dimensions define two cross-grain end surfaces characterized individually as aligned either normal to the grain or oblique to the grain; the L×W dimensions define two substantially parallel top and bottom surfaces; and, a majority of the W×H surfaces in the mixture of wood particles have end checking.

STATEMENT OF GOVERNMENT LICENSE RIGHTS

This invention was made with government support by the Small BusinessInnovation Research program of the U.S. Department of Energy, ContractSC0002291. The United States government has certain rights in theinvention.

FIELD OF THE INVENTION

Our invention relates to precision wood particle mixtures manufacturedby rotary bypass shear comminution of wood chip raw materials.

BACKGROUND OF THE INVENTION

“Wood chips” are small pieces of wood of generally uniform size andshape produced from fresh tree trunks and limbs by mechanical treatment(chipping) with sharp tools such as knives. Wood chips typically have aparallelepiped shape with six rhombus faces and a low and consistentthickness compared to length and width dimensions. Length along thegrain direction is generally 5 to 50 mm (0.2 to 2 inches). Thecross-grain ends are smoothly cut (chipped) at an oblique angle toinduce chip formation at appropriate thickness. Particular sizes andshapes of chips have long been standardized as feedstocks for pulp andpaper production, particleboard manufacture, and other industrial uses.For example, chips for pulp and paper manufacturing generally maximizeintact fibers and fiber bundles along the grain between chipper-cutends. Several generations of chipping equipment have been developed toproduce such wood-chip feedstocks. However, conventional wood chips arenot optimal as direct feedstocks for many biomass conversion processes.

In the case of biofuel production it is preferable to maximize diffusionand heat-transfer distances both across and along the grain. It is alsopreferable to cut across the fiber bundles rather than preserve theirnatural length. In addition, many biofuel processes require smallfeedstock particle sizes. Re-comminution of wood chips has introducedprocessing concerns. Milling and grinding affects biomass particle shapeas well as size. The hammer mill process tends to break wood chipsmultiple times along the grain, initially into narrow sticks (aka, pinchips) and eventually into narrower fiber bundles that tend to retainthe full chip length. Likewise, grinding, wet milling, and crushing tendto separate fibers without cutting across the grain. Such comminutionmachines often require dry chips, at 15% wet wood basis (wwb) or less,yet drying woody biomass below its fiber saturation point, approximately40-45% wwb (˜30% dry basis), is an energy intensive process that mayincrease feedstock recalcitrance during conversion processing.

Thus, it would be advantageous to provide comminuted wood-chip particleswith properties more favorable to biomass conversion processing.

SUMMARY OF THE INVENTION

We have applied engineering design principles to develop a low-energycomminution process that produces a new class of wood particlefeedstocks from wood chips and hog fuel.

Representative embodiments include mixtures of wood particles havingfibers aligned in a grain, wherein: the wood particles are characterizedby a length dimension (L) aligned substantially parallel to the grain, awidth dimension (W) normal to L and aligned cross grain, and a heightdimension (H) normal to W and L; the L×H dimensions define two sidesurfaces characterized by substantially intact longitudinally arrayedfibers; the W×H dimensions define two cross-grain end surfacescharacterized individually as aligned either normal to the grain oroblique to the grain; the L×W dimensions define two substantiallyparallel top and bottom surfaces; and a majority of the W×H surfaces inthe mixture of wood particles have end checking Representativeembodiments are shown in FIGS. 1B and 1C. The subject wood particlespreferably have a retained field moisture content of greater than 30%dry basis.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a photograph of of 100-gram portions of three comminutedDouglas fir chip subsamples: A, wood chips (prior art); B, one-pass woodparticles; and C, two-pass wood particles;

FIG. 2 is a perspective view of a prototype rotary bypass shear machinesuitable to produce wood particles of the present invention;

FIG. 3 (Prior Art) is a photograph of two industrial wood chip startingmaterials, (A) Douglas fir fuel grade chips and (B) whole-treeeucalyptus chips;

FIG. 4 is a photgraph of 100-gram portions of four comminuted eucalyptuschip subsamples: A, wood chips (prior art); B, one-pass; C, two-pass;and D, three-pass;

FIG. 5 shows particle size distribution data for the Douglas fir (A) andeucalyptus (B) subsamples shown in FIGS. 1 and 4; and,

FIG. 6 shows representative examples of the two cross-gain end surfacesthat predominantly characterize the subject wood particles: A, asmoothly cut chip-like beveled surface, aligned normal to grain, withtight fiber ends; and B, a sheared surface, aligned oblique to grain,characterized by end checking.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The term “grain” as used herein refers generally to the arrangement andlongitudinally arrayed direction of fibers within plant biomassmaterials. “Grain direction” is the orientation of the long axis of thedominant fibers in a piece of plant biomass material.

The terms “checks” or “checking” as used herein refer to lengthwiseseparation and opening between plant fibers in a biomass feedstockparticle. “Surface checking” may occur on the lengthwise surfaces aparticle (particularly on the L×W surfaces); and “end checking” occurson the cross-grain ends (W×H) of a particle.

The term “extent” as used herein refers to an outermost edge on aparticle's surface taken along any one of the herein described L, W, andH dimensions (that is, either parallel or normal to the grain direction,as appropriate); and “extent dimension” refers to the longest straightline spanning points normal to the two extent edges along thatdimension. “Extent volume” refers to a parallelepiped figure thatencompasses a particle's three extent dimensions.

The term “skeletal surface area” as used herein refers to the totalsurface area of a biomass feedstock particle, including the surface areawithin open pores formed by checking between plant fibers. In contrast,“envelope surface area” refers to the surface area of a virtual envelopeencompassing the outer dimensions the particle, which for discussionpurposes can be roughly approximated to encompass the particle's extentvolume.

The term “field moisture content” refers to wood chips and hog fuelmaterials that retain a harvested moisture content above theapproximately 30% (dry basis, db) fiber saturation point below which thephysical and mechanical properties of wood begin to change as a functionof moisture content. Such a wood material has not been dried below itsfiber saturation point and then rehydrated, e.g., by soaking in water.

The adjectives “green” and “seasoned” indicate wood chips and hog fuelmaterials having moisture contents of more than or less than 19% db,respectively.

The term “disc” refers to a circular object having a uniform thickness(Td) between two opposing flat sides of equal diameter. Td isconveniently measured with an outside caliper.

The new class of wood particles described herein can be readilyoptimized in size and shape for particular end-user processes andspecifications.

We have found it very convenient to use wood chips as a raw material.Our preferred manufacturing method is to feed green wood chips one ormore times into a rotary bypass shear with the grain direction orientedrandomly to the feed direction through the machine's processing head.

The rotary bypass shear that we designed for manufacture of woodfeedstock particles is a shown in FIG. 2. This prototype machine 10 ismuch like a paper shredder and includes parallel shafts 12, 14, each ofwhich contains a plurality of cutting disks 16, 18. The disks 16, 18 oneach shaft 12, 14 are separated by smaller diameter spacers (not shown)that are the same width or greater by 0.1 mm thick than the cuttingdisks 16, 18. The cutting disks 16, 18 may be smooth 18, knurled (notshown), and/or toothed 16 to improve the feeding of wood chips 20through the processing head 22. Each upper cutting disk 16 in thedepicted rotary bypass shear 10 contains five equally spaced teeth 24that extend 6 mm above the cutting surface 26. The spacing of the twoparallel shafts 12, 14 is slightly less than the diameter of the cuttingdisks 16, 18 to create a shearing interface. In our machine 10, thecutting disks 16, 18 are approximately 105 mm diameter and the shearingoverlap is approximately 3 mm.

This rotary bypass shear machine 10 used for demonstration of themanufacturing process operates at an infeed speed of one meter persecond (200 feet per minute). The feed rate has been demonstrated toproduce similar particles at infeed speeds up to 2.5 meters per second(500 feet per minute).

The width of the cutting disks 16, 18 establishes one facet of theparticles produced since the wood 20 (veneer is shown in this view) issheared at each edge 28 of the cutters 16, 18. Thus, wood particles fromour process are of more uniform size than are wood-chip particles fromshredders, hammer mills and grinders that tend to split the chips grainwise. The desired length of the facets is set into the rotary bypassshear machine 10 by either installing cutters 16, 18 having widths equalto the desired output facet length or by stacking assorted thinnercutting disks 16, 18 to the appropriate cumulative cutter width.

Fixed clearing plates 30 ride on the rotating spacer disks to ensurethat any particles that are trapped between the cutting disks 16, 18 aredislodged and ejected from the processing head 20.

We have found that frictional and Poisson forces that develop as thewood chip material 20 is sheared at a cutter edge 28 tend to create endchecking that greatly increases the skeletal surface areas of theparticles.

The subject wood particle feedstocks are described in more detail below.

A Uniform Size Distribution Profile

Two industrial wood chip raw materials, shown in FIG. 3, were comminutedby rotary bypass shear, and the particle size distributions of theresulting feedstocks were determined.

One starting material was fresh whole-tree Douglas fir fuel-grade chipsthat were destined for industrial power generation. As shown in FIG. 3A,these fuel chips were exceptionally clean, uniform, and mostlybark-free.

A sample of these fuel chips (53% wwb; as determined using the moisturecontent protocol described below) was subdivided into subsamples forprocessing through a Crumbler™ machine equipped with 3/16″ (4.8 mm)cutters.

One subsample that was not processed (“no-pass”) was reserved as acontrol. A second subsample was gravity fed in random orientationsthrough the cutting head a single time (“one-pass”). A third subsamplewas passed through the cutting head twice (“two-pass”), that is, the rawchips were comminuted a first time, and then the comminuted material wassent through the cutting head in random orientations a second time.

Prior to size sorting, each of the three subsamples was dried toconstant weight at 110° F. (43° C.). FIG. 1 is a photograph of 100-gramportions of these three dried softwood subsamples: A, no-pass; B,one-pass; and C, two-pass.

The dried subsamples were each size sorted on a Gilson® tapping sieveshaker, Sieve Screen Model No. SS-12R. Size distribution profiles werecharacterized by shaking ˜500 or 1000 g of each subsample for 10 minutesin a stacked assembly of 3 inch, 1½ inch, ½ inch, ¼ inch, No. 8, No. 16,and Pan screens having the nominal sieve size openings noted in the “mm”column in the Table 1, which shows the resulting data (expressed asweight (g) and portion (%) of starting material retained on eachscreen).

TABLE 1 No pass 1 pass 2 pass Sieve mm g % g % g % 3 inch 75.00 0 0 0 00 0 1½ inch 37.50 10.45 2.3 0 0 0 0 1 inch 25.00 85.28 18.6 0 0.7 0 0 ½inch 12.50 246.01 53.6 6.19 33.4 1 0.1 ¼ inch 6.30 92.50 20.2 313.9558.6 70.11 7.2 No. 8 2.36 19.57 4.3 550.63 5.4 775.35 79.3 No. 16 1.182.38 0.5 51.08 1.9 99.70 10.2 Pan 0 2.76 0.6 18.27 100 31.51 3.2 Total458.96 100 940.11 100 977.75 100 Shown in 1A 1B 1C FIG.

The other starting material was fresh whole-tree eucalyptus chipsdestined for hammermilling into pellet furnish. As shown in FIG. 3B, theeucalyptus chips were relatively heterogeneous in size, shape, andanatomical content (with stringy bark and leaves). A sample of theseeucalyptus chips (51% wwb) was subdivided and processed as describedabove, except that a fourth subsample was processed three times (“3pass”) through the cutting head. The subsamples were then dried asdescribed above. FIG. 4 is a photograph of 100-gram portions of thesefour dried hardwood subsamples: A, no-pass; B, one-pass; C, two-pass;and D, three-pass.

Each of the subsamples was size sorted as described above, except that awider array of screen sizes were used, as indicated in Table 2, whichsummarizes the particle size distributions of the four subsamples.

TABLE 2 Grams retained on each screen (g) Sieve mm No pass 1 pass 2 pass3 pass 1 inch 25.00 36.2 2.2 4.5 0 ½ inch 12.50 79.4 8.9 12.2 0.6 ⅛ inch9.53 59.3 8.8 9.3 1.7 ¼ inch 6.30 78.6 56.3 41.0 14.1 No. 4 4.75 31.357.1 59.8 30.7 No. 8 2.36 32.6 76.4 145.0 122.0 No. 10 2.00 4.2 9.7 22.822.5 No. 16 1.18 6.4 15.4 39.3 44.9 No. 20 0.84 2.6 5.9 15.3 17.6 Pan 08.2 10.1 22.1 22.4 Shown in FIG. 4A 4B 4C 4DThe data from Tables 1 and 2 are depicted on a percentage basis in FIGS.5A and 5B, respectively.

Several observations are noteworthy. First, these comminution resultswere achieved with green wood chips (>50% wwb), in contrast totraditional hammer milling which requires that wood chips be first driedto less than ˜15% wwb. Typically, the energy equivalent of more than 10%of the greenwood being milled will be consumed as fuel for the dryerburner.

Second, the comminuted subsamples had tighter size distribution profilesthan the raw wood chips. Furthermore, the size distribution profilestended to tighten further with multiple passes. It is axiomatic thatsuch feedstock size uniformity enables greater optimization of biofuelproduction processes.

Third, the size distribution profiles of the comminuted subsamples ofboth wood materials were similar, which indicates that this comminutionprocess (wherein each piece is sheared only once, by a uniform distance)effected uniform comminution of both the clean softwood chips and theanatomically more heterogeneous, stringy hardwood chips.

Fourth, the tighter size distribution profiles of the cumminutedsubsamples tended to cluster around the 4.8 mm width of the cutters(indicated by the arrows the FIGS. 5A and 5B). We have observed thatsuch peaks in feedstock size uniformity can be selectively shifted up ordown, as required for particular end users, by processing wood chipswith larger or smaller cutter widths, respectively. Moreover, the numberof passes through the cutting head can be selected to adjust andoptimize the particle size distribution profile of the comminutedfeedstock. Referring to FIG. 5B, for example, two passes achieved anominal 4.8 mm no-pass target better than either one pass or threepassses.

Thus, the invention provides precision wood particle mixturescharacterized by a substantially uniform size distribution profile asdetermined by the following protocol: drying 1000 g of the wood particlemixture to constant weight at 110° F.; pouring approximately 300-400 gof the dried wood particles into a stacked screen assembly selected fromamong the Coarse, Medium, and Fine assemblies shown in Table 3 (below);shaking the stacked screen assembly for 10 minutes on a motorizedtapping sieve shaker; weighing the wood particles that are retained oneach of the screens; and determining that the wood particles arecharacterized by a substantially uniform size range if the sum of theweights of wood particles retained on any contiguous five of the screensexceeds 80% of the poured total. Preferably, the sum of the weights ofwood particles retained on any contiguous three of the screens exceeds90% of the poured total.

TABLE 3 Coarse Medium Fine top Screen Sieve Screen Sieve Screen Sieve ↓Size (mm) Size (mm) Size (mm) 1 3 inch 75.00 1 inch 25.00 ⅜ inch 9.53 21½ inch 37.5 ½ inch 12.50 No. 4 4.75 3 1 inch 25.00 ⅜ inch 9.53 ⅛ inch3.18 4 ½ inch 12.50 ¼ inch 6.30 No. 10 2.00 5 ¼ inch 6.30 No. 4 4.75 No.16 1.19 6 ⅛ inch 3.18 No. 8 2.38 No. 20 0.84 7 No. 16 1.18 No. 10 2.00No. 35 0.50 8 Pan 0.00 No. 16 1.19 No. 50 0.30 9 No. 20 0.84 No. 1000.15 10  Pan 0.00 Pan 0.00 ↑ bottom

A Shape Distribution Profile Favorable to Flowability

Biomass piece shape is an increasingly important quality parameter forcomminuted biomass. Shape affects flowability and performance ofmaterials handling systems, pretreatment, and rate of conversion. Thefollowing observations address flowability.

Shape assessments were made of the three Douglas fir subsamples shown inFIG. 1. Some 100+ particles were randomly collected from each subsample,and extent particle dimensions were measured with a digital caliper:length (L) along the grain, width (W) normal to L and aligned crossgrain, and thickness (T) normal to W and L. Particle weight was measuredwith an electronic balance.

Table 4 summarizes the particle dimensions (mm) and weight (g) data ofthe three subsamples. The calculated average (mean) values are indicatedin underlined type, the standard deviations by italics, and thecoefficients of variation (i.e., mean/SD) in bold type.

TABLE 4 Length Width Thickness Wt. Shown in Douglas fir n = (L) (W) (T)(g) FIG. Raw Whole 120 28.08  13.53  3.91 1.03 1A Tree Chips 13.27 11.47  2.64 2.12 1.18 1.48 Single Pass, 132 14.49  6.61 3.62 0.23 1B3/16″ Cutters 8.77 2.76 1.60 1.65 2.40 2.26 Double Pass, 117 9.88 4.022.22 0.10 1C 3/16″ Cutters 6.43 1.88 1.24 1.54 2.14 1.80

Several observations are noteworthy. First, rotary bypass shear ofrandomly oriented wood chips produces small and uniformly shapedparticles. A chip is cut just one time during each pass-through thecutting head, at a predetermined distance set by the cutter width, andthe tumultuous infeed orientation randomly positions the cut across thechip's L, W, and T dimensions. In contrast, milling and grinding tend toseparate fibers without cutting across the grain.

Referring to Table 4, particle length (L) was reduced by half in thefirst pass and further reduced in the second pass. We have observed thatparticle length converges on the cutter width (4.8 mm in this example)as the number of passes increases following a power law function.

Particle width (W) rapidly converged to the cutter width. Here, widthwas reduced by half in the first pass and was further reduced toapproximately the cutter width (4.8 mm) in the second pass.

Because the no-pass chip thickness (T) was initially less than thecutter width, this dimension was not as materially reduced as the L andW dimensions. Thus, the uniform minimum distance to center (thickness)of the wood chip raw material was substantially maintained.

The net effect is smaller, more uniformy shaped wood particle mixturesthat can be readily optimized to meet particular end-user processspecifications, by “tuning” the rotary bypass shear comminution oflocally available chipped materials with empirically selected cutterwidth size(s) and pass-through number(s).

Biomass conversion systems require flowable feedstocks to continuouslyintroduce biomass materials from ambient conditions into a controlledreactor environment. Here, the combination of size and shape uniformitywith consistent reduction in particle length favors feedstockflowability. Flow is the relative movement of bulk particles inproximity to neighboring particles or along the wall of a container orstorage tank. Steady and reliable flow of industrial feedstocks isdesirable.

Particle size and shape affect the flowability of biomass feedstocks.Generally stated, the smaller the particle size, and the more sphericalthe particle shape, the better the flow; for example, small cubes flowbetter than sticks. For biomass particles, the dimensional length/width,length/thickness, and thickness/width ratios are useful indexes of thedegree of tendency toward sphericity. Decreasing the L/W, L/T, and T/Wratios of a biomass raw material during comminution will tend to enhanceflowability of the resulting feedstock. Consistency in particle shapeand size is also important, as relatively long particles tend to bridgeand interrupt flow, and so variations in particle length should beminimal.

The following Table 5 converts the dimensional data of Table 4 into suchaverage ratios (underlined) with standard deviations (italics) andcoefficients of variation (bold).

TABLE 5 Shown in Douglas fir n = L/W L/T T/W FIG. Raw Whole 120 3.149.15 3.48 1A Tree Chips 2.26 6.72 1.78 1.40 1.36 1.96 Single Pass, 1322.55 4.55 2.03 1B 3/16″ Cutters 1.74 3.07 0.97 1.47 1.48 2.09 DoublePass, 117 2.82 5.07 2.07 1C 3/16″ Cutters 2.43 2.97 0.98 1.16 1.71 2.11

Several observations are noteworthy. First, the single-pass particleswere smaller and mass (Table 4), and exhibited lower and tighterdimensional ratios (Table 5) than the raw wood chips. Hence, feedstockflowability would tend to increase.

Second, sending the single-pass material through the cutting head inrandom orientations a second time (Double Pass) significantly reducedparticle size and mass (Table 4) while retaining the flow enhancingconsistent roundness of the single-pass material as compared to the woodchip starting material (Table 5).

Third, length variation was reduced with each pass through the cuttinghead (Table 4), contributing to tighter L/W and L/T ratios (Table 5).

Now, to generalize these observations, mindful that the subjectfeedstocks will often be “tuned” to fulfill particular end-userspecifications, by comminuting available wood chip materials by one ormore passes through particular cutter-width arrays. However, in manyembodiments, the resulting wood particle feedstock will advantageouslyexhibit lower and tighter dimensional ratios than as observed for thealready very uniform starting material in Table 5.

Thus, the subject wood particle mixtures—when made from wood chipswherein T<L, T<W, and L>W—are preferably characterized by a shapedistribution profile conducive to flowability as determined by thefollowing protocol: drying 1000 g of the wood particle mixture toconstant weight at 110° F.; selecting at random 100 of the dried woodparticles; measuring the length and width dimensions of each of the 100wood particles; calculating a L/W value for each of the 100 woodparticles; calculating a mean, a standard deviation, and a coefficientof variation from the 100 L/W values, and determining that the woodparticles are characterized by a shape distribution profile conducive toflowability if the calculated mean is less than 3 with a coefficient ofvariance less than 2.

A Substantially Uniform Minimum Distance to Center, Favorable to HeatTransfer and Diffusion

Pulp wood chips have been optimized to have a substantially uniformthickness in order to promote consistent diffusion and batch digestionin pulping liquor. Uniformity in thickness or minimum distance to centerwill also promote consistent heat transfer in pyrolysis processing.Referring back to Table 4, it was observed that the minimum distance tocenter (thickness) of a wood chip raw material can be substantiallymaintained by selecting a cutter width that is equal to of less than theaverage thickness of the raw chips. Starting. The resulting woodparticle feedstocks will, in many embodiments, exhibit a lower andtighter minimum distance to center value than observed for the veryuniform starting material in Table 4.

Thus, the subject wood particle mixtures are preferably characterized bya substantially uniform minimum distance to center as determined by thefollowing protocol: drying approximately 1000 g of the wood particlemixture to constant weight at 110° F.; selecting at random 100 of thedried wood particles; measuring the length, width, and height dimensionsof each of the selected wood particles; selecting the smallest of thethree dimensional measurements for each particle; calculating from the100 smallest dimensional measurements a mean, a standard deviation, anda coefficient of variation value; and determining that the woodparticles are characterized by a substantially uniform minimum distanceto center if the calculated coefficient of variation value is less than3.0, and preferably less than 2.0.

A Disrupted Grain Structure Favorable to Heat Transfer and Diffusion

FIGS. 6A and 6B show representative examples of the two general types oflengthwise cross-gain end morphology that predominantly characterize thesubject comminuted particle mixtures: A, a smoothly cut beveled surfacewith tight fiber ends; and B, a sheared surface characterized bydisrupted fiber ends. (Scales are in millimeters.)

By way of illustration, a random handful of the fuel-chip one-passsubsample shown in FIG. 1B was gently shaken by hand on a No. 4 screen(4.76 mm) to remove smaller pieces (simply for convenient visualanalysis). One hundred of the retained particles were observed using amagnifying glass for end structure morphology, using the above criteriato categorize each cross-grain end as either smoothly cut with tightfiber ends, or as having disrupted fiber ends. Results are shown inTable 6, wherein “2 Chip Ends” refers to parallelepiped-shaped particles(typically chips and pin chips) having a pair of oppositively beveledcross-grain ends cut tangential to the grain with tight fibers. “1 Chip& 1 Disrupted” refers to particles with one chip-like end (“Chip”) andone cross sheared end (parallel or oblique to grain) with disruptedfiber ends (“Disrupted”). “2 Disrupted Ends” refers to particles havingtwo cross-grain ends with disrupted fibers. We observed that the theDisrupted Ends were often cut obliquely to the grain direction,resulting in a non-parallelepiped shaped particle.

TABLE 6 Particle End Grain Morphologies 2 Chip 1 Chip & 2 Disrupted Ends1 Disrupted Ends Bark Chunk Total Raw 92 0 2 5 1 100 Whole Tree ChipsOne Pass, 22 44 32 2 0 100 3/16″ Cutters

(“Bark” refers to bark particles, and “Chunk” refers to an oversizedpiece, which were not assessed in this observation.)

The Table 6 data indicates that passing wood chips in random arraythrough the cutting head produces grain disruptions such as tend toenhance diffusion and heat transfer in many biomass conversionprocesses. The net effect of shearing each chip or particle once perpass, in random orientation at one or more cutter edges is to produce afeedstock with a preponderance of obliquely sheared, disrupted ends.

Thus, the subject wood particle mixtures are generally characterized bya disrupted grain structure as determined by the following protocol:drying 1000 g of a wood particle mixture to constant weight at 110° F.;selecting at random 100 of the dried wood particles for observation;observed each cross-grain end of each selected particle to categorizeeach cross-grain end as either smoothly cut substantially parallel tograin or obliquely sheared with disrupted fiber ends; and determiningthat the wood particles are characterized by a disrupted grain structureif at least a majority of the observed cross-grain ends are obliquelysheared with end checking. Following additional passes through thecutter head, a substantial majority of the W×H surfaces in the mixtureof wood particles will exhibit end checking conducive to heat transferand diffusion.

Retained Field Moisture Content Above the Fiber Saturation Point

In order to avoid biomass recalcitrance during conversion processing, abiomass feedstock should retain its field moisture content. The term“field moisture content” refers to wood chips and to comminutedfeedstocks produced therefrom that retain a harvested moisture contentabove the approximately 30% fiber saturation point below which thephysical and mechanical properties of wood begin to change as a functionof moisture content. Such a wood material has not been dried below itsfiber saturation point and then rehydrated, e.g., by soaking in water.

Thus, the subject wood particle feedstocks are preferably characterizedby a retained field moisture content greater than 30% dry weight basis,as determinable for example by the following protocol.

Moisture Content Determination Protocol Definitions

Fine Material—Material where the largest 10% of the mass appearsvisually to be less than 10 mm (0.4 inches) in length.

Coarse Material—Material where the largest 10% of the mass appearsvisually to be less than 200 mm (8 inches) in length.

Large Material—Material where the largest 10% of the mass appearsvisually to be greater than 200 mm (8 inches) in length.

Drying Container:

Use an oven safe container rated to at least 121° C. (250° F.). Ensurethat the container prevents cross sample contamination and is labeledwith the sample identification number. Appropriate containers may be acolander lined with a large coffee filter, small coffee filters placedin a muffin pan, or an edged baking sheet. Multiple samples may beplaced on a tray for ease of handling, provided that each sample isindependently contained, labeled, and removable for weighing.

Procedure:

-   -   1. Preheat oven to 105° C. (221° F.).    -   2. Determine the tare weight of the container including the        liner, if used, without material in the container.        -   a. Weigh the container (and liner).        -   b. Record the container (and liner) weight to the nearest            0.1 grams, as the “Tare Weight.”    -   3. Place the sample material into the container.    -   4. Weigh and record the combined weight of the material and        container (and liner if used), as the “Gross Wet Weight.”    -   5. Place container into the oven and dry for the appropriate        time listed below in the Initial Drying Time section.    -   6. At the initial drying time weigh and record the mass of the        sample (including container, liner, and material), as “Gross        Weight TH” where T is the initial drying time in hours.    -   7. Return the material to the oven for a minimum of one        additional hour.    -   8. After the additional time period weigh and record mass of the        sample (including container, liner, and material), as “Gross        Weight TH” where T is the time in hours since sample started        drying (do not subtract the time out of the oven for weighing).        Return the sample to the oven and calculate the moisture content        as described below in the Moisture Content Calculation section.        -   a. If the change in moisture content is 1% or less, the            sample is dry. Record the combined weight of the material,            container, and liner as “Gross Dry Weight. Record the            moisture content as “Moisture Content Final. Remove the            sample from the oven and store as appropriate.        -   b. If the change in moisture content is greater than 1%            repeat steps 7-8 and record the moisture content as            “Moisture Content TH” where T is the time in hours since            sample started drying.            Initial Drying Time:

Fine Material—Material where the largest 10% of the mass appearsvisually to be less than 10 mm (½ inch) in thickness shall have aninitial drying time of 4 hours.

Coarse Material—Material where the largest 10% of the mass appearsvisually to be greater than 10 mm (½ inch) in thickness shall have aninitial drying time of 24 hours.

Filtrate Material—Material that is removed from a slurry shall have aninitial drying time of 8 hours.

Moisture Content Calculation:

-   -   1. Calculate the Net Wet Weight by subtracting the Tare Weight        from the Gross Wet Weight.    -   2. Calculate the Net Dry Weight by subtracting the Tare Weight        from the last Gross Weight recorded.    -   3. Calculate the moisture content using the equation below.        MC _(wwb)=[(W _(wet) −W _(dry))/W _(wet)]×100        -   where:            -   MC_(wwb)=Moisture Content Wet Basis (i.e., % wwb)            -   W_(wet)=Net Wet Weight            -   W_(dry)=Net dry weight

Low Energy Comminution

Specific energy consumption for reprocessing whole-tree chips through arotary shear appears to consume less than half the energy that would berequired by a knife mill, grinder, hammer mill, or other attrition milldevice. Data are shown in our provisional patent application No.61/663,367, which is incorporated herein by reference in its entirety.In an operational setting, multipass shearing can be directly coupledwhere output from a first processing head (1-pass) feeds directly into asecond processing head (2-pass) equipped with smaller cutter widths thanthe first.

While the preferred embodiment of the invention has been illustrated anddescribed, it will be appreciated that various changes can be madetherein without departing from the spirit and scope of the invention.

We claim:
 1. An industrial feedstock comprising a mixture of woodparticles having fibers aligned in a grain, wherein: the wood particlesare characterized by a length dimension (L) aligned substantiallyparallel to the grain, a width dimension (W) normal to L and alignedcross grain, and a height dimension (H) normal to W and L; the L×Hdimensions define two side surfaces characterized by substantiallyintact longitudinally arrayed fibers; the W×H dimensions define twocross-grain end surfaces characterized individually as aligned eithernormal to the grain or oblique to the grain; the L×W dimensions definetwo substantially parallel top and bottom surfaces; a majority of theW×H surfaces in the mixture of wood particles have end checking; and,the mixture of wood particles is characterized by a substantiallyuniform size distribution profile as determined by the followingprotocol: drying approximately 1000 g of the wood particles to constantweight at 110° F.; pouring 400 g of the dried wood particles into astacked screen assembly consisting of in a contiguous size-orderedarray: a top 1-inch screen having 25.00 mm nominal sieve openings, a½-inch screen having 12.50 mm nominal sieve openings, a ⅜-inch screenhaving 9.53 mm nominal sieve openings, a ¼-inch screen having 6.30 mmnominal sieve openings, a No. 4 screen having 4.74 mm nominal sieveopenings, a No. 8 screen having 2.38 mm nominal sieve openings, a No. 10screen having 2.00 mm nominal sieve openings, a No. 16 screen having1.19 mm nominal sieve openings, a No. 20 screen having 0.84 mm nominalsieve openings, and a bottom pan; shaking the stacked screen assemblyfor 10 minutes on a motorized tapping sieve shaker; weighing the woodparticles that are retained on each of the screens; and determining thatthe wood particle mixture is characterized by a substantially uniformsize range if the sum of the weights of wood particles retained on anycontiguous five of the screens exceeds 320 g in total.
 2. The industrialfeedstock of claim 1, wherein the sum of the weights of wood particlesretained on any contiguous three of the screens exceeds 360 g in total.3. The industrial feedstock of claim 1, wherein the wood particles arecharacterized by a retained field moisture content of greater than 30%dry basis.
 4. An industrial feedstock comprising a mixture of woodparticles having fibers aligned in a grain, wherein: the wood particlesare characterized by a length dimension (L) aligned substantiallyparallel to the grain, a width dimension (W) normal to L and alignedcross grain, and a height dimension (H) normal to W and L; the L×Hdimensions define two side surfaces characterized by substantiallyintact longitudinally arrayed fibers; the W×H dimensions define twocross-grain end surfaces characterized individually as aligned eithernormal to the grain or oblique to the grain; the L×W dimensions definetwo substantially parallel top and bottom surfaces; a majority of theW×H surfaces in the mixture of wood particles have end checking; and,the mixture of wood particles is characterized by a shape distributionprofile conducive to flowability as determined by the followingprotocol: drying 1000 g of the wood particle mixture to constant weightat 110° F.; selecting at random 100 of the dried wood particles;measuring the length and width dimensions of each of the 100 woodparticles; calculating a L/W value for each of the 100 wood particles;calculating a mean, a standard deviation, and a coefficient of variationfrom the 100 L/W values, and determining that the wood particles arecharacterized by a shape distribution profile conducive to flowabilityif the calculated mean is less than 3 with a coefficient of varianceless than
 2. 5. The industrial feedstock of claim 4, wherein the woodparticles are characterized by a retained field moisture content ofgreater than 30% dry basis.
 6. An industrial feedstock comprising amixture of wood particles having fibers aligned in a grain, wherein: thewood particles are characterized by a length dimension (L) alignedsubstantially parallel to the grain, a width dimension (W) normal to Land aligned cross grain, and a height dimension (H) normal to W and L;the L×H dimensions define two side surfaces characterized bysubstantially intact longitudinally arrayed fibers; the W×H dimensionsdefine two cross-grain end surfaces characterized individually asaligned either normal to the grain or oblique to the grain; the L×Wdimensions define two substantially parallel top and bottom surfaces; amajority of the W×H surfaces in the mixture of wood particles have endchecking; and, a majority of the wood particles are characterized by asubstantially uniform minimum distance to center as determined by thefollowing protocol: drying approximately 1000 g of the wood particlemixture to constant weight at 110° F.; selecting at random 100 of thedried wood particles; measuring the length, width, and height dimensionsof each of the 100 particles; selecting the smallest of the threedimensional measurements for each particle; calculating from the 100smallest dimensional measurements a mean, a standard deviation, and acoefficient of variation; and determining that the wood particles arecharacterized by a substantially uniform minimum distance to center ifthe calculated coefficient of variation is less than 3.0.
 7. Theindustrial feedstock of claim 6, wherein the calculated coefficient ofvariation is less than 2.0.
 8. The industrial feedstock of claim 6,wherein the wood particles are characterized by a retained fieldmoisture content of greater than 30% dry basis.